Y5V Dielectric General Specifications Y5V formulations are for general-purpose use in a limited temperature range. They have a wide temperature characteristic of +22% 82% capacitance change over the operating temperature range of 30C to +85C. These characteristics make Y5V ideal for decoupling applications within limited temperature range. PART NUMBER (see page 2 for complete part number explanation) 0805 3 G 104 Z A T 2 A Size Voltage Dielectric Capacitance Capacitance Failure Terminations Packaging Special ( x ) 6.3V = 6 Y5V = G Code (In pF) Tolerance Rate T = Plated Ni 2 = 7 Reel Code 10V = Z Z = +80 20% A = Not and Sn 4 = 13 Reel A = Std. 2 Sig. Digits + 16V = Y Applicable Product Number of 25V = 3 Zeros 50V = 5 Capacitance Change Temperature Coefficient Insulation Resistance vs. Temperature vs. DC Bias Voltage 10,000 +20 +10 +40 0 +20 -10 1,000 0 -20 -30 -20 -40 -40 100 -50 -60 -60 -70 -80 -80 0 -100 -55 -35 -15 +5 +25 +45 +65 +85 +105 +125 +20 +30 +40 +50 +60 +70 +80 +90 0 20 40 60 80 100 Temperature C Temperature C % DC Bias Voltage 0.1 F - 0603 0.22 F - 0805 1 F - 1206 Impedance vs. Frequency Impedance vs. Frequency Impedance vs. Frequency 10,000 1,000 1,000 1,000 100 100 100 10 10 10 1 1 1 0.1 0.1 0.1 0.01 0.01 0.01 10,000 100,000 10,000 100,000 10,000,000 10,000 100,000 1,000,000 10,000,000 1,000,000 10,000,000 1,000,000 Frequency (Hz) Frequency (Hz) Frequency (Hz) 26 % Capacitance Z (Ohms) Z (Ohms) c/c (%) Insulation Resistance (Ohm-Farads) Z (Ohms)Y5V Dielectric Specifications and Test Methods Parameter/Test Y5V Specification Limits Measuring Conditions Operating Temperature Range -30C to +85C Temperature Cycle Chamber Capacitance Within specified tolerance 5.0% for 50V DC rating Freq.: 1.0 kHz 10% 7.0% for 25V DC rating Voltage: 1.0Vrms .2V Dissipation Factor 9.0% for 16V DC rating For Cap > 10 F, 0.5Vrms 120Hz 12.5% for 10V DC rating 10,000M or 500M - F, Charge device with rated voltage for Insulation Resistance whichever is less 120 5 secs room temp/humidity Charge device with 300% of rated voltage for Dielectric Strength No breakdown or visual defects 1-5 seconds, w/charge and discharge current limited to 50 mA (max) Appearance No defects Deflection: 2mm Capacitance Test Time: 30 seconds 30% Resistance to Variation 1mm/sec Flexure Dissipation Meets Initial Values (As Above) Stresses Factor Insulation Initial Value x 0.1 90 mm Resistance 95% of each terminal should be covered Dip device in eutectic solder at 230 5C Solderability with fresh solder for 5.0 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 20% Variation Dip device in eutectic solder at 260C for 60 Dissipation Resistance to seconds. Store at room temperature for 24 2 Meets Initial Values (As Above) Factor Solder Heat hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -30C 2 30 3 minutes Capacitance 20% Step 2: Room Temp 3 minutes Variation Dissipation Thermal Meets Initial Values (As Above) Step 3: +85C 2 30 3 minutes Factor Shock Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after Meets Initial Values (As Above) Strength 24 2 hours at room temperature Appearance No visual defects Charge device with twice rated voltage in Capacitance 30% test chamber set at 85C 2C Variation for 1000 hours (+48, -0) Dissipation Initial Value x 1.5 (See Above) Load Life Factor Remove from test chamber and stabilize Insulation Initial Value x 0.1 (See Above) at room temperature for 24 2 hours Resistance Dielectric before measuring. Meets Initial Values (As Above) Strength Appearance No visual defects Store in a test chamber set at 85C 2C/ Capacitance 30% 85% 5% relative humidity for 1000 hours Variation (+48, -0) with rated voltage applied. Load Dissipation Initial Value x 1.5 (See above) Humidity Factor Remove from chamber and stabilize at Insulation Initial Value x 0.1 (See Above) room temperature and humidity for Resistance 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength 27