18900 Panduit Drive TDS: GMNT Tinley Park, IL 60487 Effective Date: 16JUL12 Customer Service: 800-777-3300 Revision: 6 Technical Data Sheet High Temperature Marker Tag This specification is intended to outline the physical and chemical properties of PANDUITs GMNT material for identification purposes. Printable Material Suffixes FPT FQT FQT-B PRODUCT SPECIFICATIONS: Description: Material is RoHS compliant (European Union directive 2002/95/EC). GMNT is a crosslinked, thermal transfer printable polyolefin. When printed using RMR*BL, RMER4BL-A, and RMH*BL thermal transfer ribbons it will also meet MIL-M- 81531. This product has been tested for use as an identification marker for use in (Class 1E) harsh environments in various high temperature power plants. RMR*BL, RMER4BL-A, RMH*BL (recommended for best print Recommended Ribbons: quality) White Standard Colors: Thickness: 24 +/- 2 mils Service Temperature Range: Minus 67F to 275F (Minus 55C to 135C) Store at 70 F(21C) and 50% Relative Humidity Storage Conditions: PROPERTIES: PERFORMANCE: 1500 psi minimum (ASTM D638) Tensile Strength: Elongation Ultimate: 200% minimum (ASTM D 638) 500 volts/mil minimum (ASTM D876) Dielectric Strength: Water Absorption: 0.5% maximum (ASTM D570) Printability: Product meets print performance as per MIL-M-81531 Flammability: Product complies with the UL94-V2 flammability test Specific Gravity: 1.35 max (ASTM 792) QUV Outdoor Durability: The samples were tested in a QUV weather tester as per test procedure ASTM G-154. Observations made at *3000 hours exposure showed no loss in legend or change in material. Page 1 of 5 2007 PANDUIT Corp TDS: GMNT 18900 Panduit Drive TDS: GMNT Tinley Park, IL 60487 Effective Date: 16JUL12 Customer Service: 800-777-3300 Revision: 6 Technical Data Sheet *3000 hours equates to 5 years of assimilated outdoor UV exposure. CHEMICAL/SOLVENT RESISTANCE: The testing was conducted at room temperature. Samples were thermal transfer printed with Panduit Resin ribbon on Panduit printer. Chemical/Solvent 7 DAY IMMERSION DIP TEST RUB TEST 30% Sulfuric acid 1 1 1 10% Sulfuric acid 1 1 1 30% Hydrochloric 1 1 1 acid 10% Hydrochloric 1 1 1 acid 50% Sodium 2 1 1 Hydroxide 10% Sodium 3 1 1 Hydroxide Methyl Ethyl Ketone 3 3 3 Acetone 3 3 3 1:1:1 Trichloroethane 2 1 3 Isopropyl Alcohol 3 1 1 ASTM 3 Oil 1 1 1 SAE 30 Oil 1 1 1 Alconox 1 1 1 Toluene 2 1 3 Mineral Spirits 1 1 1 Glacial Acetic Acid 3 3 3 Diesel Fuel 1 1 1 10% Sodium 1 1 1 Chloride Water 1 1 1 Gasoline 1 1 1 1 = No change 2 = Slight failure in Legibility 3 = Failure in Legibility 7 Day Immersion Immersed in reagent for 7 days Dip Test - Five 10 minute dips in reagent followed by 30 minute recovery Rub Test - Rubbed sample for 1 minute with swab soaked in reagent Marking Performance: MIL-M-81531: Print still legible after 20 eraser rubs with hard hand pressure. Page 2 of 5 2007 PANDUIT Corp TDS: GMNT