S100X075T1D

18900 Panduit Drive TDS: GMTD1 Tinley Park, IL 60487 Effective Date: 23JUL2013 Customer Service: 800-777-3300 Revision: 7 Technical Data Sheet Self Laminating Clear Polyvinylidene Fluoride Film This specification is intended to outline the physical and chemical properties of PANDUITs pressure sensitive self laminating polyvinylidene fluoride material and include the following part numbers and printable material identifiers: Part Number Prefixes Printable Material Suffixes T1T T1J T1D PRODUCT SPECIFICATIONS: Description: Material is RoHS compliant (European Union directive 2002/95/EC). Material is a self-extinguishing top coated polyvinylidene fluoride film with a pressure sensitive adhesive. This material is used in a self- laminating format for wire/cable marking. Print Methods: This material is recommended for dot matrix, thermal transfer, laser and inkjet printing. Adhesive: Acrylic based, pressure sensitive permanent adhesive. Standard Colors: Clear film with white print-on area Thickness: 1.8 +/- 0.3 mils (substrate and adhesive) 0 0 0 0 Service Temperature Range: -65 F to 275 F(-53.9 C to 135 C) Minimum Application Temperature: 50F (10C) Storage Conditions: Store at 70F (21C) and 50% Relative Humidity. PROPERTIES: PERFORMANCE: Peel Adhesion to Stainless Steel: 30 oz/in width (PSTC-101, 15 min. dwell) 66 oz/in width(PSTC-101, 72 hours dwell) Shear Adhesion: 24+ hours (PSTC-107, Procedure A) Tensile Strength: MD 7 lbs/inch +/-0.7 lbs/inch (PSTC-131) TD 7 lbs/inch +/-0.7 lbs/inch (PSTC-131) Tack: 460 g/cm2 (ASTMD2979-71, 1 sec. dwell) MD 400% +/- 10% (PSTC-131) Elongation: TD 125% +/- 10% (PSTC-131) Elevated Temperature Exposure: After 24 hours at 160F (70C) there was no deterioration of the substrate Dielectric Strength: 1900 Volts /mil (ASTM D149-09, Method A) Flammability: Average burn time less than 10 seconds (ASTM D1000) UV Resistance: *3000 hours no change observed (ASTM G154) *3000 hours equates to 5 years of assimilated outdoor UV exposure. Page 1 of 3 2010 PANDUIT Corp TDS: GMTD1 18900 Panduit Drive TDS: GMTD1 Tinley Park, IL 60487 Effective Date: 23JUL2013 Customer Service: 800-777-3300 Revision: 7 Technical Data Sheet CHEMICAL/SOLVENT RESISTANCE: Samples were dot matrix printed with Panduit PDLR ribbon, thermal transfer printed with RMH*BL/RMEH*BL and RMR*BL/RMER*BL ribbons, laser and inkjet printed. These samples were wrapped around a 1/12 OD wire in self-laminating format. Test was conducted at room temperature after 24 hour dwell. The samples were immersed in the specified chemical reagents for 5 immersions using the following cycle: a 10 minute immersion time followed by a 30 minute recovery time. Visual Observation Chemical Reagent Substrate / Adhesive Dot Matrix Thermal Laser Printed Inkjet Printed Printed Legend Transfer Printed Legend Legend Legend Distilled Water No effect No effect No effect No effect No effect No effect No effect No effect Mineral Spirits No effect No effect No effect No effect No effect ASTM 3 Oil No effect No effect No effect No effect Isopropyl Alcohol No effect No effect No effect No effect No effect Methanol Slight adhesive bleed No effect No effect No effect No effect 3% Alconox No effect No effect No effect Detergent No effect No effect 10% Sodium No effect No effect No effect Hydroxide Solution No effect No effect 10% Sulfuric Acid No effect No effect No effect Solution No effect No effect 5% Sodium Chloride No effect No effect No effect Solution No effect No effect Freon TF No effect No effect No effect No effect No effect Super Agitene No effect No effect No effect No effect No effect Jet-A Fuel No effect No effect No effect No effect No effect Arco TruSlide 68 No effect No effect No effect No effect No effect SAE 30 Motor Oil No effect No effect No effect Page 2 of 3 2010 PANDUIT Corp TDS: GMTD1