CL10B333KB8WPNC Samsung

Specification of Automotive MLCC (Reference sheet) CL10B333KB8WPNC Supplier : Samsung electro-mechanics Samsung P/N : CAP, 33nF, 50V, 10%, X7R, 0603 Product : Multi-layer Ceramic Capacitor Description : AEC-Q 200 Specified A. Samsung Part Number CL 10 B 333 K B 8 W P N C Series Samsung Multi-layer Ceramic Capacitor Size 0603 (inch code) L: 1.6 0.1 mm W: 0.8 0.1 mm Dielectric X7R Inner electrode Ni , Open mode Soft Termination Capacitance 33 Termination Capacitance 10 % Plating Sn 100% (Pb Free) tolerance Product Automotive Rated Voltage 50 V Grade code Standard Thickness 0.8 0.1 mm Packaging Cardboard Type, 7 reel B. Reliability Test and Judgement condition Performance Test condition HiHigghh TTeempmperatueraturree AppearanceAppearance :: NoNo abnormalabnormal eexxtteeriorrior appearanceappearance UnpowUnpoweredered, 1000hrs T1000hrs T==150150 Exposure Capacitance Change : Within 10% Measurement at 242hrs after test conclusion Tan : 0.03 max IR : More than 10,000 or 500 Whichever is Smaller Temperature Cycling Appearance : No abnormal exterior appearance 1000Cycles Capacitance Change : Within 10% Measurement at 242hrs after test conclusion Tan : 0.03 max 1 cycle condition : IR : More than 10,000 or 500 -55+0/-3 (153min) -> Room Temp(1min.) Whichever is Smaller -> 125+3/-0 (153min) -> Room Temp(1min.) Destructive Physical No Defects or abnormalities Per EIA 469 Analysis Appearance : No abnormal exterior appearance Moisture Resistance 10Cycles, t=24hrs/cycle Capacitance Change : Within 12.5% Heat (25~65 ) and humidity (80~98%), Unpowered Tan : 0.03 max measurement at 242hrs after test conclusion IR : More than 10,000 or 500 Whichever is Smaller Appearance : No abnormal exterior appearance Humidity Bias 1000hrs 85 /85%RH, Rated Voltate and 1.3~1.5V, Capacitance Change : Within 12.5% Add 100kohm resistor Tan : 0.035 max Measurement at 242hrs after test conclusion The charge/discharge current is less than 50mA. IR : More than 500 or 25 Whichever is Smaller Appearance : No abnormal exterior appearance High Temperature 1000hrs TA=125 , 200% Rated Voltage, Operating Life Capacitance Change : Within 12.5% Measurement at 242hrs after test conclusion Tan : 0.035 max The charge/discharge current is less than 50mA. IR : More than 1000 or 50 Whichever is SmallerPerformance Test condition External Visual No abnormal exterior appearance Microscope (10) Physical Dimensions Within the specified dimensions Using The calipers Appearance : No abnormal exterior appearance Mechanical Shock Three shocks in each direction should be applied along Capacitance Change : Within 10% 3 mutually perpendicular axes of the test specimen (18 shocks) Tan , IR : initial spec. Peakvalue Duration Wave Velocity 1,500G 0.5ms Half sine 4.7m/sec. Appearance : No abnormal exterior appearance Vibration 5g s for 20min., 12cycles each of 3 orientations, Capacitance Change : Within 10% Use 8 5 PCB 0.031 Thick 7 secure points on one long side Tan , IR : initial spec. and 2 secure points at corners of opposite sides. Parts mounted within 2 from any secure point. Test from 10~2000 . Resistance to Appearance : No abnormal exterior appearance Solder pot : 2605 , 101sec. Solder Heat Capacitance Change : Within 10% Tan , IR : initial spec. Thermal Shock Appearance : No abnormal exterior appearance -55 /+125 . Capacitance Change : Within 10% Note: Number of cycles required-300, Tan , IR : initial spec. Maximum transfer time-20 sec, Dwell time-15min. Air-Air ESD Appearance : No abnormal exterior appearance AEC-Q200-002 Capacitance Change : Within 10% Tan , IR : initial spec. Solderability 95% of the terminations is to be soldered a) Preheat at 155 for 4 hours, Immerse in solder for 5s at 2455 evenly and continuously b) Steam aging for 8 hours, Immerse in solder for 5s at 2455 c)g) Steam agingg for 8 hours,, Immerse in solder for 120s at 2605 solder : a solution ethanol and rosin Electrical Capacitance : Within specified tolerance The Capacitance /D.F. should be measured at 25 , Characterization Tan (DF) : 0.025 max. 1 10%, 1.00.2Vrms IR(25 ) : More than 10,000 or 500 I.R. should be measured with a DC voltage not exceeding IR(125 ) : More than1,000 or 10 Rated Voltage 25 , 125 for 60~120 sec. Whichever is Smaller Dielectric Strength Dielectric Strength : 250% of the rated voltage for 1~5 seconds Appearance : No abnormal exterior appearance Board Flex Bending to the limit (2 ) for 5 seconds Capacitance Change : Within 10% Terminal Appearance : No abnormal exterior appearance 10N, for 601 sec. Strength(SMD) Capacitance Change : Within 10% Beam Load Destruction value should not be exceed Beam speed Chip Length < 2.5 0.50.05 /sec a) Chip Thickness > 0.5 : 20N b) Chip Thickness 0.5 : 8N Temperature X7R Characteristics (From -55 to 125 , Capacitance change should be within 15%) C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5 , 10sec. Max ) Meet IPC/JEDEC J-STD-020 D Standard Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. ShouldShould yyoouu havehave anyany questquestiionon regardiregardingng tthhee pproductroduct specifspecificaticationsions, please contact our sales personnel or application engineers.