Technical Data September 2014 3M Polyimide Film Tape 5413 Product Description 3M Polyimide Film Tape 5413 with DuPont Kapton polyimide film and silicone adhesive used for PCB solder masking and other high temperature applications. This product is amber colored and 2.7 mil (69 microns) thick Key Features The DuPont Kapton polyimide film does not soften at elevated temperatures, thus the film provides an excellent release surface at elevated temperatures Is dimensionally stable at high temperatures, which helps reduce rework, helping to enable high productivity Is flame retardant, chemical and radiation resistant which helps protect surfaces to help reduce replacement costs The silicone adhesives high temperature performance helps reduce adhesive transfer which helps to eliminate cleaning, enabling high productivity Polyethylene tape core instead of cardboard 3M Polyimide Film Tape 5413 Product Construction/Material Description Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. 3M Polyimide Film Tape 5413 Property Value Backing Dupont Kapton Polyimide Film Adhesive Silicone Color Amber Standard Roll Length 33 m (36yd) Applications Mask for protection of gold fingers of printed circuit boards during wave solder or solder dip process. Release surface in fabrication of parts cured at elevated temperatures. Typical Physical Properties and Performance Characteristics Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Final product specifications and testing methods will be outlined in the products Certificate of Analysis (COA) that is shipped with the commercialized product. 3M Polyimide Film Tape 5413 Property Method* Value Adhesion to Steel: D-3330 22 oz/in width (24 N/100 mm) Tensile Strength at Break: D-3579 33 lb/in width (578 N/100 mm) Elongation at Break: D-3579 62% Backing Thickness: D-3652 1.0 mil (0.03 mm) 3M Polyimide Film Tape 5413 Total Tape Thickness: D-3652 2.7 mil (0.07 mm) Temperature Use Range: - -73 to 260C (-100 to 500F) Dielectric Strength: D-149 7000 volts Outgassing: - %TLM = 1.50, %CVCM = 0.50 Flame Retardancy: Per UL-510 product category: Pass 0ANZ2 File E124809 *Methods listed as ASTM are tested in accordance with the ASTM method noted Storage and Shelf Life The shelf life of 3M Polyimide Film Tape 5413 is 36 months from the date of manufacture when stored in original cartons at 21C (70F) and 50% relative humidity. Certificate of Analysis (COA) The 3M Certificate of Analysis (COA) for this product is established when the product is commercially available from 3M. The commercially available product will have a COA specification established. The COA contains the 3M specifications and test methods for the products performance limits that the product will be supplied against. The 3M product is supplied to 3M COA test specifications and the COA test methods. Contact your local 3M representative for this products COA. This technical data sheet may contain preliminary data and may not match the COA specification limits and/or test methods that may be used for COA purposes. Final product specifications and testing methods will be outlined in the products Certificate of Analysis (COA) that is shipped with the commercialized product.