X-On Electronics has gained recognition as a prominent supplier of LD025C181KAB2A Multilayer Ceramic Capacitors MLCC - SMD/SMT across the USA, India, Europe, Australia, and various other global locations. LD025C181KAB2A Multilayer Ceramic Capacitors MLCC - SMD/SMT are a product manufactured by Kyocera AVX. We provide cost-effective solutions for Multilayer Ceramic Capacitors MLCC - SMD/SMT, ensuring timely deliveries around the world.
We are delighted to provide the LD025C181KAB2A from our Multilayer Ceramic Capacitors MLCC - SMD/SMT category, at competitive rates not only in the United States, Australia, and India, but also across Europe and beyond. A long established and extensive electronic component distribution network has enhanced our global reach and dependability, ensuring cost savings through prompt deliveries worldwide. Client satisfaction is at the heart of our business, where every component counts and every customer matters. Our technical service team is ready to assist you. From product selection to after-sales support, we strive to deliver a seamless and satisfying experience. Are you ready to experience the best in electronic component distribution? Contact X-ON Electronics today and discover why X-On are a preferred choice for the LD025C181KAB2A and other electronic components in the Multilayer Ceramic Capacitors MLCC - SMD/SMT category and beyond.
MLCC Tin/Lead Termination B X7R General Specifications AVX Corporation will support those customers for commercial and military Multilayer Ceramic Capacitors with a termination consisting of 5% minimum lead. This termination is indicated by the use of a B in the 12th position of the AVX Catalog Part Number. This fulfills AVXs commitment to providing a full range of products to our customers. AVX has provided in the following pages a full range of values that we are currently offering in this special B termination. Please contact the factory if you require additional information on our MLCC Tin/ Lead Termination B products. PART NUMBER (SEE PAGE 4 FOR COMPLETE PART NUMBER EXPLANATION) LD05 5 C 101 J A B 2 A Size Voltage Dielectric Capacitance Failure Terminations Packaging Special Capacitance LD03 - 0603 6.3V = 6 X7R = C Code (In pF) Rate B = 5% min lead 2 = 7 Reel Code Tolerance LD04 - 0504* 10V = Z 2 Sig. Digits + A = Not X = FLEXITERM 4 = 13 Reel A = Std. B = .10 pF (<10pF) with 5% min LD05 - 0805 16V = Y Number of Applicable Product C = .25 pF (<10pF) Contact Factory lead** LD06 - 1206 25V = 3 Zeros D = .50 pF (<10pF) For LD10 - 1210 35V = D F = 1% ( 10 pF) Multiples* LD12 - 1812 50V = 5 **X7R only G = 2% ( 10 pF) LD13 - 1825 100V = 1 J = 5% LD14 - 2225 200V = 2 K = 10% LD20 - 2220 500V = 7 M = 20% *LD04 has the same CV ranges as LD03. See FLEXITERM section for CV options NOTE: Contact factory for availability of Tolerance Options for Specific Part Numbers. Contact factory for non-specified capacitance values. The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order. 47 112916MLCC Tin/Lead Termination B X7R Specifications and Test Methods Parameter/Test X7R Specification Limits Measuring Conditions Operating Temperature Range -55C to +125C Temperature Cycle Chamber Capacitance Within specified tolerance 10% for 50V DC rating Freq.: 1.0 kHz 10% 12.5% for 25V DC rating Voltage: 1.0Vrms .2V Dissipation Factor 12.5% for 25V and 16V DC rating 12.5% for 10V DC rating 100,000M or 1000M - F, Charge device with rated voltage for Insulation Resistance whichever is less 120 5 secs room temp/humidity Charge device with 250% of rated voltage for 1-5 seconds, w/charge and discharge current Dielectric Strength No breakdown or visual defects limited to 50 mA (max) Note: Charge device with 150% of rated voltage for 500V devices. Appearance No defects Deflection: 2mm Capacitance Test Time: 30 seconds 12% Variation Resistance to Flexure Dissipation Meets Initial Values (As Above) Stresses Factor Insulation Initial Value x 0.3 Resistance 95% of each terminal should be covered Dip device in eutectic solder at 230 5C Solderability with fresh solder for 5.0 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 7.5% Variation Dip device in eutectic solder at 260C for 60 Dissipation Resistance to Meets Initial Values (As Above) seconds. Store at room temperature for 24 2 Factor Solder Heat hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -55C 2 30 3 minutes Capacitance 7.5% Step 2: Room Temp 3 minutes Variation Dissipation Meets Initial Values (As Above) Step 3: +125C 2 30 3 minutes Thermal Shock Factor Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after Meets Initial Values (As Above) Strength 24 2 hours at room temperature Appearance No visual defects Capacitance 12.5% Charge device with 1.5 rated voltage ( 10V) in Variation test chamber set at 125C 2C Dissipation for 1000 hours (+48, -0) Initial Value x 2.0 (See Above) Load Life Factor Insulation Remove from test chamber and stabilize at room Initial Value x 0.3 (See Above) Resistance temperature for 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Capacitance 12.5% Store in a test chamber set at 85C 2C/ 85% Variation 5% relative humidity for 1000 hours Dissipation (+48, -0) with rated voltage applied. Initial Value x 2.0 (See Above) Load Factor Humidity Remove from chamber and stabilize at room Insulation Initial Value x 0.3 (See Above) temperature and humidity for Resistance 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order. 48 112916