CHIP MONOLITHIC CERAMIC CAPACITOR MLSC SERIAL AND SOFT TERMINATION TYPE FOR AUTOMOTIVE GCE21BR72A223KA01 (0805, X7R, 22000pF, 100Vdc) : packaging code Reference Sheet 1.Scope This product specification is applied to Chip Monolithic Ceramic Capacitor MLSC Serial and Soft Termination Type used for Automotive Electronic equipment. 2.MURATA Part NO. System (Ex.) GCE 21 B R7 2A 223 K A01 L (1)L/W (2)T (3)Temperature (4)DC Rated (5)Nominal (6)Capacitance (7)Muratas (8)Packaging Dimensions Characteristics Voltage Capacitance Tolerance Control Code Code Dimensions 3. Type & Dimensions L W T MLSC design e g e (Unit:mm) (1)-1 L (1)-2 W (2) T e g 2.00.3 1.250.2 1.250.2 0.2 to 0.7 0.7 min. 4.Rated value (3) Temperature Characteristics Specifications and Test (4) (6) (Public STD Code):X7R(EIA) (5) Nominal Methods DC Rated Capacitance (Operating Temp. coeff Temp. Range Capacitance Voltage Tolerance Temp. Range) orCap. Change (Ref.Temp.) -55 to 125 C 100 Vdc 22000 pF 10 % -15 to 15 % -55 to 125 C (25 C) 5.Package mark (8) Packaging Packaging Unit f180mm Reel L 3000 pcs./Reel EMBOSSED W8P4 f330mm Reel K 10000 pcs./Reel EMBOSSED W8P4 Product specifications in this catalog are as of Apr.15,2013,and are subject to change or obsolescence without notice. Please consult the approval sheet before ordering. Please read rating and Cautions first. GCE21BR72A223KA01-01 1AEC-Q200 Murata Standard Specification and Test Methods Specification. No AEC-Q200 Test Item AEC-Q200 Test Method High Dielectric Type Pre-and Post-Stress 1 - Electrical Test 2 High Temperature The measured and observed characteristics should satisfy the Set the capacitor for 100012 hours at 1503. Set for Exposure (Storage) specifications in the following table. 242 hours at room temperature, then measure. Appearance No marking defects Capacitance R7: Within 12.5% Change D.F. R7: 0.05 max. I.R. More than 10,000M or 500 F (Whichever is smaller) 3 Temperature Cycling The measured and observed characteristics should satisfy the Fix the capacitor to the supporting jig in the same manner and under specifications in the following table. the same conditions as (19). Perform the 1000 cycle according to Appearance No marking defects the four heat treatments listed in the following table. Set for 242 Capacitance R7: Within 7.5% hours at room temperature, then measure Change Step Time(min) Temp.() D.F. R7: 0.05 max. 1 153 -55+0/-3 2 1 Room 3 153 125+3/-0 I.R. 4 1 Room More than 10,000M or 500 F (Whichever is smaller) Initial measurement for high dielectric constant type Perform a heat treatment at 150+0/-10 for one hour and then set for 242 hours at room temperature. Perform the initial measurement. 4 Destructive No defects or abnormalities Per EIA-469. Phisical Analysis 5 Moisture Resistance The measured and observed characteristics should satisfy the Apply the 24-hour heat (25 to 65) and humidity (80 to 98%) specifications in the following table. treatment shown below, 10 consecutive times. Appearance No marking defects Set for 242 hours at room temperature, then measure. Capacitance R7: Within 10.0% Humidity Humidity Temperature 8098% 8098% Humidity Humidity Humidity () Change 9098% 9098% 9098% 70 D.F. R7: 0.05 max. 65 60 55 50 45 40 35 30 25 I.R. More than 10,000M or 500 F +10 20 - 2 (Whichever is smaller) 15 10 5 Initial measuremt 0 -5 -10 One cycle 24hours 0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 Hours 6 Biased Humidity The measured and observed characteristics should satisfy the Apply the rated voltage and 1.3+0.2/-0vdc (add 6.8k resister) specifications in the following table. at 853 and 80 to 85% humidity for 100012 hours. Appearance No marking defects Remove and set for 242 hours at room temprature, then measure. Capacitance R7: Within 12.5% The charge/discharge current is less than 50mA. Change D.F. R7: 0.05 max. I.R. More than 1,000M or 50 F (Whichever is smaller) JEMCGS-02082 2