SPC22124

Solder Wire Specifications: Rosin Activated (RA) Flux: It is a high activity core flux designed for excellent instant wetting action, even on Nickel surfaces. Although it is a RA-based material, the residues are non-corrosive if not cleaned. Per J-STD-004. Classified as ROM1 flux. Water Soluble Flux: It is a high-activity water-soluble core flux for soldering difficult metals. It is designed for optimal cleanability , along with minimal smoke and odor. Its residues must be removed. It is classified as ORH1 per J-STD-004. Rosin Mildly Activated (RMA) Flux: It is an RMA based core flux that provides wetting action comparable to typical RA flux. Although it is an RMA-based material, the residues are non-corrosive if not cleaned. It is categorized as ROL1 per J-STD-004. No-Clean Flux: It is a halide-free, rosin based no-clean core flux that provides excellent wetting combined with optimal reliability and cosmetics. It is compliant to Bellcore GR-78 and is classified as ROL0 per J-STD-004. Specification Table: Diameter Acid SIR Standard Alloy Softening Number (Surface Wire Content Flux Flux Point Part Number Weight (mg- Insulation Gauge Tin/ % Type Celsius (Flux Inches mm KOH/ G Resist- (AWG) Lead Extract) Sample) ance) SPC22126 20 0.032 0.81 60/40 SPC22127 18 0.04 1.02 60/40 SPC22128 16 0.05 1.27 60/40 SPC22129 14 0.062 1.57 60/40 SPC22130 24 0.02 0.51 63/37 1Ibs. SPC22131 22 0.025 0.64 63/37 Rosin 9 3.3% 80C 150-160 >1.0 10 (RA) SPC22132 20 0.032 0.81 63/37 SPC22133 18 0.04 1.02 63/37 SPC22134 16 0.05 1.27 63/37 SPC22135 14 0.062 1.57 63/37 SPC22123 22 0.025 0.64 60/40 0.5 lbs. SPC22124 20 0.032 0.81 60/40 0.5 lbs. www.element14.com www.farnell.com www.newark.com www.cpc.co.uk www.mcmelectronics.com Page <1> 14/07/15 V1.0Solder Wire Diameter Acid SIR Standard Alloy Softening Number (Surface Wire Content Flux Flux Point Part Number Weight (mg- Insulation Gauge Tin/ % Type Celsius (Flux Inches mm KOH/ G Resist- (AWG) Lead Extract) Sample) ance) Rosin SPC22125 21 0.025 0.64 63/37 0.5 Ibs. 80C 150-160 (RA) SPC22136 20 0.032 0.81 60/40 1Ibs. Water 3.3% 60C 120-130 Soluble SPC22137 20 0.032 0.81 63/37 1Ibs. 9 >1.0 10 Rosin SPC22138 20 0.032 0.81 63/37 1Ibs. 92C 150-160 (RMA) SPC22139 20 0.032 0.81 63/37 1Ibs. No Clean 1.1% 75C 190-210 (NC600) SPC22140 24 0.02 0.51 63/37 1Ibs. Part Number Table Description Part Number SPC22126 SPC22127 SPC22128 SPC22129 SPC22130 SPC22131 SPC22132 SPC22133 Note SPC22134 The Water Soluble Solder has a flux within that must be Solder Wire SPC22135 cleaned therefore, the Flux Extract Softening Point Test does not apply. SPC22123 Acid Number test is based upon the IPC-TM-650 test method. SPC22124 Flux Appearance : Amber Solid SPC22125 SPC22136 SPC22137 SPC22138 SPC22139 SPC22140 Important Notice : This data sheet and its contents (the Information) belong to the members of the Premier Farnell group of companies (the Group) or are licensed to it. No licence is granted for the use of it other than for information purposes in connection with the products to which it relates. No licence of any intellectual property rights is granted. The Information is subject to change without notice and replaces all data sheets previously supplied. The Information supplied is believed to be accurate but the Group assumes no responsibility for its accuracy or completeness, any error in or omission from it or for any use made of it. Users of this data sheet should check for themselves the Information and the suitability of the products for their purpose and not make any assumptions based on information included or omitted. Liability for loss or damage resulting from any reliance on the Information or use of it (including liability resulting from negligence or where the Group was aware of the possibility of such loss or damage arising) is excluded. This will not operate to limit or restrict the Groups liability for death or personal injury resulting from its negligence. DURATOOL is the registered trademark of the Group. Premier Farnell plc 2012. www.element14.com www.farnell.com www.newark.com www.cpc.co.uk www.mcmelectronics.com Page <2> 14/07/15 V1.0